[2015-Vol.12-Issue 2]Structural and Mechanical Characterization of Atrina Pectinata and Freshwater Mussel Shells
发布时间: 2015-06-05 04:47  点击:2051

Volume 12, Issue 2, April 2015, Pages 276–284

  • a School of Mechanical Engineering and Automation, Beihang University, Xueyuan Road No. 37, Haidian District, Beijing 100191, China
  • b International Research Institute for Multidisciplinary Science, Beihang University, Xueyuan Road No. 37, Haidian District, Beijing 100191, China

Abstract

The microstructures of Atrina pectinata and freshwater mussel shells are investigated by optical microscopy and scanning electron microscopy. The mechanical properties of these shells are characterized by nanoindentation and three-point bending tests. Results show that both shells possess a prismatic microstructure mainly composed of columnar crystals and an organic matrix. The fracture toughness of the prismatic structure of Atrina pectinata and freshwater mussel are approximately 1.15 MPa·m1/2 and 0.87 MPa·m1/2, respectively, while the fracture toughness of natural calcite is approximately 0.2 MPa·m1/2. Calculated results from indentations agree with those obtained from the three-point bending tests. The columnar crystal material shows excellent fracture toughness due to grain refinement. In addition, the organic matrix of the prismatic layer can arrest cracks, and thereby improves the fracture toughness.

Keywords

  • shell
  • prismatic
  • fracture toughness
  • organic matrix
  • crack
  •  

Full text is available at http://www.sciencedirect.com/science/article/pii/S1672652914601207 

Address: C508 Dingxin Building, Jilin University, 2699 Qianjin Street, Changchun 130012, P. R. China
Copyright © 2024 International Society of Bionic Engineering All Rights Reserved
吉ICP备11002416号-1